Can someone link me a replacement lead screw I'm sick of anycubic playing riddles with me would this work

Check this out at Amazon.com
Iverntech NEMA 17 Stepper Motor with Integrated 310mm T8 Lead Screw for RepRap Prusa i3 3D Printers Z Axis or CNC Machine https://www.amazon.com/…/ref=cm_sw_r_other_apa_T30oBbCQ0BBQG

翻譯年糕

Opinions needed. What is causing the stripes on the miniatures cape? All other areas are smooth. Over curing? Too little supports? Printed in 45 degree angle, face up

翻譯年糕

Hope the new Photon X can print at this scale! :p

翻譯年糕

I am definitely a newb myself. I'm on week 5 now and around 80 prints. These recent prints have maxed out the z height, so I am doing pretty big prints that take 12-15 hours at .05 layers.

Here's what I found and my experience... again this is just my experience...
I have had zero 3D printing experience before getting the Photon. I've had print failures, but none of the failures were due to a fault of the printer, it was something I did wrong with the supports (or forgetting to shake my resin!)

This printer far exceeds my skills and abilities (right now) but I am learning :)

翻譯年糕

Hello, I need some guidance.

I have jeweler designs I have created that I can print with the castable resins.

I would like to know what all equipment and parts needed to be able to create a burnout mold, and then use it to create silver and gold pieces.

翻譯年糕

50µ Card 28.3ºc 2/2

翻譯年糕

Flint Read , Chad Elstad . I could not add this video to the other post for some reason. As I was saying in the other post, the brass mount appears to be fine... at least the one in the arm bracket has been working for the month or so I was able to use the printer. This video should hopefully show you the problem.

翻譯年糕

No more broken minis from dropping off the table, or brittle mecanical parts, the Flexi is coming soon in 3 differents flex level. You can use it neat or mix it to your favorite Rapid color.

翻譯年糕

Hi, Thanks for adding me so quickly! My main interest is jewelry - does anybody have any close up pictures of 10 micron prints they would care to share?

翻譯年糕

Rev.180709

From the short tests i've done, this resin has a great potencial for a reasonable price. Better details in the negative space than anycubic black and about the same exposure sweet spot/range. Both me and Toby Kirkby found that the resin is quite fragile to IPA exposure easily cracking and becoming brittle, maybe the best solvent to use is rubbing alcohol or something other like tek with ultrassonic cleaner further tests needed.

PRINTER: PHOTON:PN10A32XX8097

Test method: Exposure Card; Limit validation prints with ameralabs town (thinguiverse)
Tester: X3msnake

RESIN INFORMATION
Cost per kg: 62.eur | Density: N/A | Shrinkage: 0,75% (N/T) | Washing solvent: IPA seems to be too strong and causes cracking easily (more tests needed)

OBSERVATION TESTS
Smell: Less than anycubic but slightly noticable | Color pre-cure: Deep Black | Viscosity: Less than anycubic (180-200cps@25º - N/T)

EXPOSURE TESTS
50µ CARD 28.3ºc > Exposure sweet spot: 10s | Exposure range: 8-18s | Detail holding: Very good at negative space. fine positive spaces need longer exposures at cost of losing negative details

VERIFICATION TESTS
Minimum Exposure time for light supports (0.4mm tip) @50µ: 12s

POST CURE TESTS
Color post-cure: Deep Black IPA stains the resin | Burn test (does it leave ash): N/T | Suitable for casting: N/T | Hardness: 85 Shore D (N/T) | Tensile strenght: N/A - N/T | Break force: N/A - N/T | Heat resistance: N/A - N/T

Representative in the group: Andrius AmeraLabs

-----
N/A - Not Available